Recovery Compressive Strength Aluminum Fiber Light Weight Concrete After Burning With Variation Of Water Curing Time

Download573 downloads
  • @INPROCEEDINGS{10.4108/eai.24-10-2018.2280573,
        author={Antonius Mediyanto and Bambang Santosa and Edy Purwanto and Jb. Irawan S.W.},
        title={Recovery Compressive Strength Aluminum Fiber Light Weight Concrete After Burning With Variation Of Water Curing Time},
        proceedings={The 1st International Conference on Computer Science and Engineering Technology Universitas Muria Kudus},
        publisher={EAI},
        proceedings_a={ICCSET},
        year={2018},
        month={11},
        keywords={water curing light weight concrete burning},
        doi={10.4108/eai.24-10-2018.2280573}
    }
    
  • Antonius Mediyanto
    Bambang Santosa
    Edy Purwanto
    Jb. Irawan S.W.
    Year: 2018
    Recovery Compressive Strength Aluminum Fiber Light Weight Concrete After Burning With Variation Of Water Curing Time
    ICCSET
    EAI
    DOI: 10.4108/eai.24-10-2018.2280573
Antonius Mediyanto1,*, Bambang Santosa1, Edy Purwanto1, Jb. Irawan S.W.1
  • 1: Universitas Sebelas Maret
*Contact email: mediyantoantonius@gmail.com

Abstract

The research concerns on strenght of light weight concrete with aluminum fiber as micro-reinforcement by enviromental load especially burning and water curing. The purpose of this study was to determine the minimum time of water curing to obtain a minimum compressive strength of 100.00% recovery. In this research cylindrical concrete of 150 mm dia 300 mm high for compressive test. Fiber volume fraction are 0,75% of concrete. Aluminum fiber with aspect ratio 50, cement type I, sand, alwa, water, and viscocrete are used. Testing are based on SK SNI M–14–1989–F [1]. The result shows that the minimum time to recovery of lightweight concrete compressive strength with water curing is 42 days, while for aluminum fiber lightweight concrete to recovery compressive strength is 28 days. Water curing can self healing light weight concrete and aluminum fiber light weight concrete after burning